- Determination of the Compositional Fluctuation of TiB<SUB>2</SUB>-ZrB<SUB>2</SUB> Solid Solution
- ZrB2 TiB2ケイ コヨウタイ ノ ソセイ ヘンドウ テイリョウ
この論文をさがす
抄録
A method to estimate compositional fluctuation in (Ti1-x, Zrx) B2 system using a value of the width of the fluctuation of lattice spacing was developed. This system forms a complete solid solution. All the compositions have hexagonal symmetry. The fluctuations of lattice spacings of (hk·0) planes and (00·l) planes have different values, because the dependencies of a-spacing and c-spacing on the composition are different. The compositional fluctuation was determined from the measured values of the fluctuation of the lattice spacings. Effect of the mechanical strain on the determination of the compositional fluctuation was examined, because the mechanical strain also affects the measured values of the fluctuation of lattice spacings. The examination showed that the mechanical strain can be neglected in this measurement. Relation between measured compositional fluctuation and composition showed that (Ti0.5Zr0.5) O3 had largest compositional fluctuation for samples prepared under the same conditions. (Ti1-x, Zrx) B2 by spark plasma sintering had smaller compositional fluctuation compared with those by hot press sintering.
収録刊行物
-
- Journal of the Society of Inorganic Materials, Japan
-
Journal of the Society of Inorganic Materials, Japan 14 (326), 26-33, 2007
無機マテリアル学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205389968128
-
- NII論文ID
- 10018284739
-
- NII書誌ID
- AA11416367
-
- ISSN
- 13453769
- 21854378
-
- NDL書誌ID
- 8643312
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可