- NISHIDA Toshihiko
- Department of Chemistry, Kyoto Institute of Technology
-
- SHIONO Takeshi
- Department of Chemistry, Kyoto Institute of Technology
-
- YAMAUCHI Hiroyuki
- Department of Chemistry, Kyoto Institute of Technology
-
- NISHIKAWA Tomozo
- Department of Chemistry, Kyoto Institute of Technology
Bibliographic Information
- Other Title
-
- MgO‐SiCウイスカー複合セラミックスの破壊エネルギ
- MgO SiC ウイスカー フクゴウ セラミックス ノ ハカイ エネルギ
Search this article
Description
In order to develop MgO base ceramics having higher thermal shock resistance for MHD plant use, ceramic composites of MgO reinforced with 15 and 20wt% of SiC whisker were fabricated by the hot-pressing at 1800°C and 1900°C under 200kg/cm2 for 30min. The effective fracture energy (γeff) of the hot-pressed composites and MgO were measured by work of fracture technique using chevron notched specimens over the range from room temperature to 1400°C. Up to 1000°C, the γeff values of the composite ceramics were slightly lager than those of the hot-pressed MgO. At temperatures above 1000°C, the γeff values of the composites increased remarkably, and were about 3-7times higher than those of hot-pressed MgO at 1400°C.<br>The mechanism of the increase in γeff values were discussed on the basis of the load-deflection behavior in bending fracture, the chemical reaction of SiC whisker with MgO matrix and the fracture surface morphology.
Journal
-
- Journal of the Society of Materials Science, Japan
-
Journal of the Society of Materials Science, Japan 36 (400), 17-21, 1987
The Society of Materials Science, Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001205391111168
-
- NII Article ID
- 110002296988
-
- NII Book ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL BIB ID
- 3119052
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed