Evaluation of Fatigue Crack Propagation by Using Effective Stress Intensity Factor Range.

DOI Web Site

Bibliographic Information

Other Title
  • 有効応力拡大係数範囲ΔＫｅｆｆによる疲労き裂伝ぱ挙動の評価に関して
  • ユウコウ オウリョク カクダイ ケイスウ ハンイ デルタ Keff ニ ヨル

Search this article

Description

Fatigue crack propagation law in the following two cases was investigated under the negative stress ratio R(=σmin/σmax) condition. The one is the crack propagation in the field of welding-residual stress, and the other is that after the overloading. In the former case, the crack propagation rate da/dN depended on the stress ratio R. Due to the tensile residual stress, the crack propagation rate increased as the stress ratio decreased in the range of 0≤R≤-2. In the latter case, the crack propagation rate da/dN after the overloading was higher at first and then became lower than that of the constant stress amplitude. In the present experimental cases, the crack propagation rate was affected by the residual stress and the overloading. However, the crack propagation behavior had a good correlation with the crack closure behavior. Therefore, in the present cases, the crack propagation law was reasonably evaluated with the effective stress intensity factor range ΔKeff.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top