Long-term stress relaxation properties of SUS 316 stainless steel.

DOI Web Site 1 Citations

Bibliographic Information

Other Title
  • ＳＵＳ３１６鋼の長時間応力リラクセーション特性
  • SUS316 コウ ノ チョウジカン オウリョク リラクセーション トクセイ

Search this article

Abstract

The understanding of stress relaxation behavior is important to evaluate the safety and reliability of structural materials used in high temperature plants. In this study, the long-term stress relaxation behavior was investigated for SUS 316 stainless steel at 500°C to 750°C. The residual stress gradually increased in the stress relaxation test below 550°C. On the other hand, the residual stress rapidly decreased after testing for 1000 to 3000hr above 600°C. The increase of residual stress at 550°C was caused by thermal densification due to the drop of carbon content in matrix accompanying the precipitation of carbide. The rapid decrease of residual stress at 650°C was caused by lowering of creep resistance due to the drop of Mo content in matrix accompanying the precipitation of Laves phase.

Journal

Citations (1)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top