軸対称引張荷重を受けるぜい性材料円板におけるき裂伝ぱ形態

DOI Web Site

書誌事項

タイトル別名
  • Crack propagation pattern in a disk of brittle material under axisymmetrical tension.
  • ジク タイショウ ヒッパリ カジュウ オ ウケル ゼイセイ ザイリョウ エンバ

この論文をさがす

説明

Crack propagation and branching behavior in a disk under axisymmetrical tension was analyzed by using an energy consideration. The result was compared with the experimental result of flexual test in which a glass or ceramic disk was supported along its edge and load was applied at the center of disk.<br>If crack branching occurs by the decrease of free energy of the system, the crack length ai after the i-th crack branching has occurred is given as follows:<br>ai≈22i+1/(2i+1-1)·Eγ/πσ2<br>Where E is elastic modulus, γ is surface energy, σ is tensile stress, and n=2i+1 is number of cracks. The surface energy γ, which was calculated by dividing the stored strain energy in a disk before fracture by the total crack surface, was almost the same independently of the number of cracks. The crack branching pattern observed for disk specimens agreed relatively well with the pattern calculated from the above equation.

収録刊行物

  • 材料

    材料 39 (441), 687-693, 1990

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ