ＣＦＲＰ積層のモードＩおよび混合モードにおける層間はく離疲労き裂伝ぱ挙動

DOI Web Site 被引用文献2件

書誌事項

タイトル別名
  • Mode I and mixed-mode propagation of delamination fatigue cracks in CFRP laminates.
  • CFRP セキソウバン ノ モード 1 オヨビ コンゴウ モード ニ オケル

この論文をさがす

抄録

Near-threshold growth of delamination fatigue cracks was investigated in unidirectional laminates made from Ciba Geigy prepregs 914C both under mode I and mixed mode of I and II. Double cantilever beam specimens (DCB) were used for mode I tests. Cracked lap shear specimens (CLS) were used for mixed mode tests. The stress ratio, R, of the minimum to maximum stress was kept constant in the tests, and the constant value was between 0.1 and 0.5. Cyclic load was shed automatically by keeping maximum displacement constant. In the region of rates above about 1-5×10-10m/cycle, the crack growth rate is expressed as a power function of fracture mechanics parameters. Below this region, there exists the growth threshold for both mode I and mixed mode. When compared at the same value of fracture mechanics parameters, the crack growth rate for mixed mode is higher than that for mode I. The values of crack growth threshold under mixed mode were smaller than those under mode I. The influence of the stress ratio becomes smaller when the crack growth rate is correlated to the energy release rate range than when the crack growth rate is correlated to the stress intensity range or the maximum energy release rate. The relative contributions of the maximum stress and of the cyclic stress on the crack growth rate are discussed on the bases of fractographic observation and mechanism consideration. The contribution of the maximum stress was high.

収録刊行物

  • 材料

    材料 36 (402), 222-228, 1987

    公益社団法人 日本材料学会

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ