- Formation of the Silicate Layers on the Nylon 6 Film by Sol-Gel Method.
- ゾル ゲルホウ ニ ヨル ナイロン フィルム エ ノ シリカ ハクマク ノ チョウセイ
この論文をさがす
説明
Silicate layer was prepared on the nylon 6 film by sol-gel method. Effect of reaction conditions on the various properties, such as layer thickness, surface morphology and the water vapor permeation rates were examined. Increasing sol-gel reaction time gives a increasing silicate layer thickness. However because of the roughness of the surface produced due to the 3-dimensional siloxane network formation in sol-gel reaction system occurred at a longer reaction time, the water vapor permeation rate was high. Addition of DMF in sol-gel reaction system controlled the drying of coated film and suppressed the shrinkage of silicate layer resulting in the smooth crack-free layers. When UV was irradiated on the sol-gel reaction system, the surface of the coated film was rather smooth and the coated film gave a fairly high barrier to water vapor, although the thickness of the layer was rather small.
収録刊行物
-
- 材料
-
材料 51 (12), 1299-1305, 2002
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205392184064
-
- NII論文ID
- 110002301816
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 6404761
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可