ＳＵ３０４の高温疲労き裂伝ぱに及ぼす予クリープ疲労損傷の影響

DOI Web Site

書誌事項

タイトル別名
  • Effect of Pre-Creep Damage on Crack Propagation of Type 304 Stainless Steel in High Temperature Fatigue.
  • SUS304 ノ コウオン ヒロウ キレツ デンパ ニ オヨボス ヨ クリープ

この論文をさがす

抄録

Creep fatigue tests were conducted on smooth specimens of a Type 304 stainless steel under a tensile stress hold (cp-type) condition at 1073K, and pre-creep damage was introduced in the form of small intergranular cracks distributed uniformly through the thickness. Macrocrack propagation tests in the high temperature fatigue were then carried out with the pre-damaged specimens. The results obtained are summarized as follows:<br>(1) The pre-damage accelerated the successive macrocrack propagation in cp-type fatigue at 923K for an equal value of creep J-integral range, ΔJc, which governs the crack propagation rate of virgin material in time dependent fatigue.<br>(2) Although the crack propagation rate of pre-damaged material in cp-type fatigue at 1073K was faster than that at 923K for ah equal ΔJc, it coincided with that of virgin one. The multiple small cracks were found on the specimens of virgin material as well as pre-damaged one near the macrocrack, which implied that the small cracks were generated not only in prior creep fatigue but also during the propagation test. Thus, the acceleration in cp-type is caused by the small cracks.<br>(3) The crack propagation rate of pre-damaged material in cycle dependent (pp-type) fatigue was nearly 10 times faster than that of virgin one. The observation of crack morphology revealed that the accelerated fatigue crack propagation was caused by the coalescence with intergranular small cracks.

収録刊行物

  • 材料

    材料 42 (474), 290-296, 1993

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ