Ｓｉ３Ｎ４の繰返し混合モード荷重下でのき裂伝ぱ挙動

DOI Web Site

書誌事項

タイトル別名
  • Crack Propagation Behavior of Si3N4 Ceramic Under Cyclic Mixed-Mode Loading.
  • Si3N4 ノ クリカエシ コンゴウ モード カジュウカ デ ノ キレツ デン

この論文をさがす

抄録

Fracture behavior of Si3N4 ceramic was investigated under cyclic mode I/mode II mixed-mode loading in various environments. The crack propagation rate was higher than that for cyclic mode I loading, and it was higher in water than in nitrogen gas. The fretting and hydration reaction seemed more active than those for cyclic mode I loading, and therfore even if the stress shielding effects by particle bridging and wedging exist, those effects were easily decreased, and the effective stress intensity factor range ΔKtip was increased. When the debris was accumlated by the fretting between the crack surfaces, the substantial effective stress intensity factor for mode II was increased. Therefore, it was suggested that in the case that KI was decreased by the particle bridging and KII was increased by the fretting the fracture morphology became transgranular fracture rather than interglanular fracture.

収録刊行物

  • 材料

    材料 43 (492), 1127-1133, 1994

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ