- Brittle Fracture of Notched Ductile Polymers
- エンセイ コウブンシ ザイリョウ ノ キリカキ ゼイセイ
この論文をさがす
抄録
To study brittle fracture of ductile polymers, tensile tests were conducted on cylindrical bars of polycarbonate, poly (vinyl chloride) and polyethylene with a circular round notch. The notchless specimens of these polymers fractured in a ductile manner after necking, but when the plastic constraint due to local yielding at the notch root became above a critical value they showed brittle fracture. Morphological observations revealed that the fracture origins were a microvoid for polycarbonate and poly (vinyl chloride) and a number of microcracks for polyethylene. They were considered to be nucleated by a hydrostatic stress component caused by plastic constraint ahead of the fully developed plastic deformation zone at the notch section.
収録刊行物
-
- 材料
-
材料 28 (311), 759-764, 1979
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205392990208
-
- NII論文ID
- 110002301143
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 2060231
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可