- Corrosion fatigue crack growth behavior of dual-phase stainless steel in synthetic sea water.
- ジンコウ カイスイチュウ ニ オケル タイ カイスイ 2ソウ ステンレス コウ
この論文をさがす
抄録
The corrosion fatigue crack growth rate of dual-phase stainless steel SUS329J1 has been measured in synthetic sea water at various stress ratios and stress cycle frequencies under free corrosion and a cathodic potential. In air the roughness-induced wedge effect enlarges the region II in the load-strain hysteresis loop. In synthetic sea water, the corrosion products-induced wedge effect under free corrosion and the Ca and Mg deposites-induced wedge effect under a cathodic potential are conspicuous, thereby enlarging the region II and raising Kop. Under free corrosion the stress assisted dissolution accerelates the crack growth rate at a low ΔKeff. In addition, at a high ΔKeff at R=0.1 and f=0.17Hz the crack growth rate is much more accerelated due to hydrogen embrittlement. Under a cathodic potential, ΔKth is remarkably high. But the crack growth rate is much accerelated due to hydrogen embrittlement in terms of ΔKeff.
収録刊行物
-
- 材料
-
材料 36 (409), 1104-1109, 1987
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205393049600
-
- NII論文ID
- 110002301331
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DyaL1cXisFaluw%3D%3D
-
- ISSN
- 18807488
- 05145163
- http://id.crossref.org/issn/05145163
-
- NDL書誌ID
- 3157637
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可