書誌事項
- タイトル別名
-
- Temperature dependence of embrittlement of Al-Ga system alloys.
- Al Gaケイ ゴウキン ノ ゼイカ ノ オンド イゾンセイ
この論文をさがす
抄録
Embrittlement of Al-Ga alloys, containing upto 25wt% Ga, was investigated by the tensile tests at various temperatures, optical microscope and SEM observation methods. The results obtained are as follows.<br>(1) At the range of temperature from -40°C to 100°C, the fracture stress of pure Al and Al-5wt% Ga alloy decreased slowly with increasing temperature, but that of alloys containing more than 10wt% Ga, even in solid solution, rapidly decreased at the range of temperature from 0°C to 30°C.<br>(2) The elongation of pure Al and Al-5wt% Ga alloy increased with increasing temperature, but that of Al-10wt% Ga alloy dropped suddenly over the range of temperature from 0°C to 30°C, and the elongation of Al-17wt% Ga alloy was little at the range of all over the testing temperature.<br>(3) The fracture of pure Al and Al-5wt% Ga alloy was of plastic type, but that of Al-10wt% Ga alloy was an intergranular cracking.<br>(4) The elongation of Al-10wt% Ga alloy increased with increasing temperature above 100°C.<br>From the above results, it is clear that the embrittlement trough exists in the solid solution Al-Ga alloy.
収録刊行物
-
- 材料
-
材料 34 (376), 70-75, 1985
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205393089792
-
- NII論文ID
- 110002301285
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 3021572
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可