Ｘ線材料強度　　クロムめっき部材の熱処理による耐食性低下のメカニズムと低下防止策

DOI Web Site 参考文献13件

書誌事項

タイトル別名
  • X-Ray Study on Deformation and Fracture of Solid. Mechanism of Decrease in Corrosion Resistance of Cr Plated Parts Due to Heat Treatment and Measures to Prevent Decrease.
  • クロムメッキ ブザイ ノ ネツ ショリ ニ ヨル タイショクセイ テイカ ノ メカニズム ト テイカ ボウシサク

この論文をさがす

説明

The mechanism of decrease in the corrosion resistance of Cr plated parts when they are subjected to a heating process and measures to prevent the decrease are studied. When the post finishing is performed after the Cr plating process, cracks in the Cr layer are closed as a result of plastic flow on the topmost surface layer. When the residual stress in the Cr layer becomes compressive due to the post finishing, the cracks are completely closed, resulting in a high corrosion resistance. The residual stress in the Cr layer changes from compressive to tensile following heat treatment. When the residual stress becomes tensile, the cracks in the Cr layer which were closed during the post finishing open once again, resulting in a decrease in the corrosion resistance. We speculated that the change of residual stress from compressive to tensile is caused by the shrinkage of the Cr layer due to heat treatment, and the difference in the coefficients of thermal expansion between the substrate (steel) and Cr layer, as well as the release of residual stress generated during processing. In order to prevent the decrease of corrosion resistance under heat treatment, it is effective to apply compressive stress, which exceeds the level of change in residual stress due to heat treatment, to the Cr layer during the post finishing, after the Cr plating process.

収録刊行物

  • 材料

    材料 51 (7), 749-755, 2002

    公益社団法人 日本材料学会

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ