欠陥のある材料の高温疲労強度

DOI Web Site

書誌事項

タイトル別名
  • The Influence of Temperature on the Fatigue Strength of Steel Containing Thermal Cracks
  • ケッカン ノ アル ザイリョウ ノ コウオン ヒロウ キョウド

この論文をさがす

説明

In order to evaluate the degree to which thermal cracks in a shaft produced from Ni-Cr-Mo steel would lower the fatigue strength, fatigue tests were carried out at room temperature, 300°C and 500°C under rotating bending.<br>We have obtained the following facts through the experiments:<br>(1) The strength reduction factor of thermal crack is about 3.5 at room temperature, 3.3 at 300°C and 2.1 at 500°C. As for the explanation of these results, it appears reasonable to assume that notch sensitivity decreases with the increase of temperature and material around the tip of thermal crack is strengthened through work hardning by repeated load and aging.<br>(2) The fatigue strength of specimens containing thermal cracks at 500°C could be improved by 50per cent through shot-peening.

収録刊行物

  • 材料試験

    材料試験 9 (84), 576-579, 1960

    公益社団法人 日本材料学会

詳細情報 詳細情報について

問題の指摘

ページトップへ