- Damage in CFRP Laminates due to Repetitive Low-Energy Impacts.
- テイエネルギ ノ クリカエシ ショウゲキ ニ ヨル CFRP セキソウザイ ノ
この論文をさがす
説明
A simple experimental method of repeated low-energy impact was devised to provide some insights into the impact damage behavior of CFRP laminates. The macroscopic failure mode and the internal damage as a consequence of repeated impacts were investigated, at some different levels of incident impact energy, with the laminated specimens prepared from different stacking sequences. The results indicated that there existed a critical incident impact energy which led to the delamination and the critical size of delamination which produced the degradation of residual strength. The delamination behavior in the laminated specimens depended largely upon the level of incident impact energy. The stiffer the specimen, the larger the delamination.
収録刊行物
-
- 材料
-
材料 44 (500), 625-630, 1995
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205393552512
-
- NII論文ID
- 110002292873
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 3608043
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可