- Superplastic Behavior of Hyper-Eutectic Al-Si P/M Alloys Produced by Centrifugal Atomization Process.
- エンシン フンムホウ ニ ヨル カキョウショウ Al Siケイ P M ゴウキ
この論文をさがす
説明
Rapidly solidified hyper-eutectic Al-25Si and Al-15Si pre-alloy powders have been produced at the cooling rate of 105-104°C/s using a centrifugal atomization process. The powders have been consolidated via hot extrusion with a reduction ratio of 110 at 490°C after vacuum hot pressing. Superplasticity of the P/M extruded bars has been investigated in the temperature range between 350 and 523°C.<br>The values of maximum elongation of Al-25Si and Al-15Si P/M extruded bars are 154% and 307%, respectively. The above P/M extruded bars show the maximum elongation at a temperature just below the solidus line of the Al-Si alloys. A filament-like elongated microstructure is formed on the surface of the P/M extruded bar under the optimum condition of superplastic deformation. The formation of such a microstructure is considered to be based on the grain boundary sliding resulting from superplastic deformation. The elongation of the P/M extruded bar, which was directly extruded without pre-compaction of the powder by vacuum hot pressing, is larger than that of the extruded bar through vacuum hot pressing.
収録刊行物
-
- 材料
-
材料 44 (500), 608-613, 1995
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205393555712
-
- NII論文ID
- 110002292870
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DyaK2MXmslehtbY%3D
-
- ISSN
- 18807488
- 05145163
- http://id.crossref.org/issn/05145163
-
- NDL書誌ID
- 3616349
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可