遠心噴霧法による過共晶Al‐Si系P/M合金の超塑性特性

書誌事項

タイトル別名
  • Superplastic Behavior of Hyper-Eutectic Al-Si P/M Alloys Produced by Centrifugal Atomization Process.
  • エンシン フンムホウ ニ ヨル カキョウショウ Al Siケイ P M ゴウキ

この論文をさがす

説明

Rapidly solidified hyper-eutectic Al-25Si and Al-15Si pre-alloy powders have been produced at the cooling rate of 105-104°C/s using a centrifugal atomization process. The powders have been consolidated via hot extrusion with a reduction ratio of 110 at 490°C after vacuum hot pressing. Superplasticity of the P/M extruded bars has been investigated in the temperature range between 350 and 523°C.<br>The values of maximum elongation of Al-25Si and Al-15Si P/M extruded bars are 154% and 307%, respectively. The above P/M extruded bars show the maximum elongation at a temperature just below the solidus line of the Al-Si alloys. A filament-like elongated microstructure is formed on the surface of the P/M extruded bar under the optimum condition of superplastic deformation. The formation of such a microstructure is considered to be based on the grain boundary sliding resulting from superplastic deformation. The elongation of the P/M extruded bar, which was directly extruded without pre-compaction of the powder by vacuum hot pressing, is larger than that of the extruded bar through vacuum hot pressing.

収録刊行物

  • 材料

    材料 44 (500), 608-613, 1995

    公益社団法人 日本材料学会

被引用文献 (3)*注記

もっと見る

参考文献 (13)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ