Characteristics of Stage 2 Fatigue Crack Growth in Ti-6Al-4V Alloy and Its Fractgraphy.

DOI Web Site

Bibliographic Information

Other Title
  • Ｔｉ‐６Ａｌ‐４Ｖ合金の疲労き裂進展特性と破面解析
  • Ti 6Al 4V ゴウキン ノ ヒロウ キレツ シンテン トクセイ ト ハメ

Search this article

Abstract

The characteristics of the stage 2 fatigue crack growth was investigated in Ti-6Al-4V alloy, in order to clarify the influence of microstructure and stress ratio. The fatigue tests were carried out at the stress ratio, R, of 0.1, 0.5 or 0.8 by using annealed (AR) and solution treatment-and-aged (STA) materials. The microstructure of AR material was coarse and anisotrophic in comparision with that of STA material.<br>The fracture surface and the cross section of fatigue cracks were observed on both materials, and the relationship between the da/dN-ΔKeff curve and the observed results were discussed.<br>(1) The da/dN of AR material was lower than that of STA material because the fatigue crack grew zigzag.<br>(2) The ΔKeff·th at R=0.8 in AR material was higher in comparison with those at other stress ratios because the secondary cracks with a length of about 100μm were generated.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top