微小な疲労き裂の伝ぱに対する一つのモデル

DOI Web Site

書誌事項

タイトル別名
  • A model for propagation of small fatigue cracks.
  • ビショウ ナ ヒロウ キレツ ノ デンパ ニ タイスル 1ツ ノ モデル

この論文をさがす

説明

The growth behavior of small fatigue cracks is clearly different from that of long fatigue cracks. In this paper, a growth law of small fatigue cracks is proposed based on the stochastic damage accumulation model for long fatigue crack growth. It contains the following three parts. (1) The growth rate of small crack growing in a grain is proportional to some power of the process region which is limited by the grain boundary. (2) A transgranular small crack propagates into the next grain over the grain boundary, when the stress is beyond the fatigue limit. (3) A small crack growing through the noncontinuum propagation begins the continuum one, when the plastic zone size of crack tip becomes larger than the average grain size. Many experimental facts about small fatigue cracks are explained on the basis of this growth law.

収録刊行物

  • 材料

    材料 37 (420), 1071-1076, 1988

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ