応力-ひずみ曲線の巨視的非線型欠陥モデル

DOI Web Site

書誌事項

タイトル別名
  • Macroscopic Nonlinear-Defect Model of Stress-Strain Curve
  • オウリョク-ヒズミ キョクセン ノ キョシテキ ヒセンケイ ケッカン モデル

この論文をさがす

説明

The nonlinear-defect model, which had been previously proposed to analyze fracture and residual strain theoretically, was applied to the real stress (σ)-strain (ε) curve of steel. The results obtained are as follows<br>(1) When it is assumed that the cross-sectional area decreases and the stress-ccncentration appears during the final fracture resulting from propagation of a visual crack, a σ-ε curve becomes similar to that of a nonlinear-defect.<br>(2) The three regions of strain in a σ-ε curve were analyzed and discussed. The equivalent defects in the initial region Ri should be different from those in the final region Rf, and at the character of equivalent defects in the transient region Rt should change from that in Ri to that in Rf. The σ-ε curve can be given as<br>ε{1-β(ε)ε}=A(ε)σ<br>where β and A are parameters characteristic of each region.<br>(3) The above expression represents quantitatively the actual σ-ε curve of steel.

収録刊行物

  • 材料

    材料 22 (233), 117-121, 1973

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ