書誌事項
- タイトル別名
-
- Environment Assisted Crack Propagation in Zr-Based Bulk Metallic Glass
- Zrキ バルク キンゾク ガラス ノ カンキョウ ジョチョウ キレツデンパ
この論文をさがす
抄録
Crack propagation tests on a bulk metallic glass, Zr55Cu30Ni5Al10, were conducted either in aqueous sodium chloride (NaCl) solutions or high purity water under sinusoidal cyclic loading or sustained loading. Although the crack growth rate in high purity water was almost identical to that in air, the rate in NaCl solution was much higher than that in air even in a very low concentration of NaCl such as 0.01%. In 3.5% NaCl solution, the time-based crack propagation rate during cyclic loading, da/dt, was determined by the maximum stress intensity factor, Kmax, but was almost independent of the loading frequency and the stress ratio, and the rate was close to that of environment-assisted cracking under a sustained load.
収録刊行物
-
- 材料
-
材料 58 (3), 219-224, 2009
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205417641472
-
- NII論文ID
- 130002085563
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 10215414
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可