Corrosion Wear Behavior of Aluminum Alloys in Contact with Rubber

DOI Web Site 4 References

Bibliographic Information

Other Title
  • ゴムと接触するアルミニウム合金の腐食摩耗挙動
  • ゴム ト セッショクスル アルミニウム ゴウキン ノ フショク マモウ キョドウ

Search this article

Abstract

It will be common understanding that soft material is worn off under wear test with hard material. However, there is possibility that hard material can be wear-damaged by soft material under particular circumstances. In the present study, wear damage behavior of aluminum alloy with rubber contact pad was investigated in air, water and 10% CaCl2 solution. The hard aluminum alloy A6061 was not damaged in the wear test with the soft rubber under air and water. However, the aluminum alloy A6061 was significantly worn in the wear test with rubber contact pad under 10% CaCl2 solution, while the cast aluminum alloy AC4C was not seriously worn. The significant wear in A6061 aluminum alloy would be caused by high Cu content and low Si content compared to the cast AC4C alloy. High Cu and low Si contents resulted in grain boundary corrosion under 10% CaCl2 solution and sliding contact of rubber will enhanced corrosion wear.

Journal

References(4)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top