- Micro-Macro Simulation of Type III and Type IV Creep Damage in 2 1/4Cr-1Mo Steel Welds
- 2 1/4Cr-1Mo鋼溶接部Type3およびType4クリープ損傷のミクロ・マクロシミュレーション
- 2 1 4Cr 1Mo コウ ヨウセツブ Type3 オヨビ Type4 クリープ ソンショウ ノ ミクロ マクロ シミュレーション
この論文をさがす
抄録
A simulation method of the creep damage progress combining the random fracture resistance model and FEM elastic-creep analysis was proposed and was applied to the evaluation of Type III and Type IV creep damage respectively in the coarse and fine grain heat affected zone (HAZ) in welded joints of 2 1/4Cr-1Mo steel. Firstly following the previous work on the fine grain HAZ, parameters for the coarse grain HAZ were identified for simulating the increase of number density of small defects on the basis of the random fracture resistance modeling. Secondly the simultaneous damage simulation for both fine and coarse grain HAZ was applied to both the welded joint model test and the burst test of elbow. A possibility of predicting the final failure time of welded joint was also discussed on the basis of the effective stress against the final failure surface. The proposed simulation successfully reproduced the increase of the number density of small defects in the fine and the coarse grain HAZ, and could predict the failure time of welded joints.
収録刊行物
-
- 材料
-
材料 56 (2), 106-113, 2007
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205417788800
-
- NII論文ID
- 130002085931
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 8689039
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可