  • Plastic Deformation of Aluminum Bicrystals having Σ7 and Σ21 Coincidence Tilt Boundary
  • シグマ 7 オヨビ シグマ 21 ケイカク タイオウ リュウカイ オ ユウスル

この論文をさがす

抄録

Three types of isoaxial symmetrical bicrystals and their component single crystals were tested in tension to clarify the effect of grain boundary on plastic properties. The <111> oriented bicrystal was deformed by the mode similar to that of the <111> oriented single crystal. Fine multiple slips which appeared from the early stage of the deformation was suppressed at the boundary. It was found that the flow stress of this bicrystal was almost equal to that of the component single crystal and the effect of grain boundary on the flow stress did not appear.<br>In two bicrystals having. Σ7 and Σ21 coincidence tilt boundary respectively, each flow stress was increased by the presence of boundary. The boundary strength was rapidly increased from yield point to about 0.5% strain by the interaction between primary slips and additional slips in the vicinity of the boundary, and it was scarcely increased from about 1.0% to 5.0% strain.<br>It was pointed out that the effect of grain boundary on the flow stress of a bicrystal is prominent by introducing multiple slips near the grain boundary in the stage-I region of the component single crystal but not prominent in the stage-II region. The effect of grain boundary on the flow stress is negligible after multiple slips take place.

収録刊行物

  • 材料

    材料 28 (305), 119-125, 1979

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ