一部分がＳｉＣ粒子とＡｌ２Ｏ３ウィスカで強化されたＡｌ鋳造合金の強度評価とフラクトグラフィ

DOI 機関リポジトリ Web Site 参考文献9件

書誌事項

タイトル別名
  • Strength Evaluation of Aluminium Cast Alloy Locally Reinforced by SiC Particles and Al2O3 Whiskers and Its Fractography
  • イチブブン ガ SiC リュウシ ト Al2O3 ウィスカ デ キョウカサレタ Al チュウゾウ ゴウキン ノ キョウド ヒョウカ ト フラクトグラフィ

この論文をさがす

抄録

In this paper, fracture mechanisms under monotonic and cyclic load and its stress distribution of an aluminum cast alloy locally reinforced by SiC particles and Al2O3 whiskers are investigated experimentally and numerically. The material is monotonically and cyclically deformed to failure at room temperature. The fracture origin and the fracture path are investigated on the fracture surfaces. The fracture occurs in the reinforced part under both monotonic and cyclic loads. SEM analysis of the fracture surface shows that the fatigue fracture is controlled by the fracture of coarse Al2O3 whiskers. On the other hand the static fracture (monotonic loading) shows that the fracture mechanism is the combination of reinforcing particle fracture and interfacial debonding between reinforcing ceramics and matrix metal. The stress distributions around the boundary between the reinforced part and unreinforced part are calculated based on an inclusion array model considering the microscopic inhomogeneous effects. Both the experimental results and the finite element simulation results show that the critical location for fracture is changed by the external stress level which controls the local stress distribution through plastic constraint between reinforcing particle and matrix alloy.

収録刊行物

  • 材料

    材料 56 (11), 1016-1021, 2007

    公益社団法人 日本材料学会

参考文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ