Effect of Laser Power Density and Scanning Speed on Residual Stress in Laser-Peened Aluminum Alloy

DOI Web Site 1 Citations 13 References

Bibliographic Information

Other Title
  • レーザピーニング処理したアルミニウム合金の残留応力のレーザパワー密度および走査速度依存性
  • レーザピーニング ショリ シタ アルミニウム ゴウキン ノ ザンリュウ オウリョク ノ レーザパワー ミツド オヨビ ソウサ ソクド イゾンセイ

Search this article

Abstract

Laser peening has recently been developed as a surface modification technique. When a high-energy laser pulse irradiates a material surface submerged in water, high-pressure plasma is generated immediately on the surface. The plasma induces an impulse wave that penetrates into the surface layer. In the present study, a laser beam of diameter about 10mm is converged by the converging lens with focal length of 250mm, and irradiates the aluminum surface. The second harmonic generation of Yttrium-Aluminum-Garnet (YAG) laser was used at a pulse frequency of 10 Hz. The effect of laser power density and scanning speed on residual stress in the laser peened aluminum alloy surface was investigated by X-ray diffraction. The following results were obtained : (1) compressive residual stress was induced in the surface of all samples ; (2) many fused traces and many micro-cracks were formed in laser peened aluminum surface ; (3) for the series of experiments with the fixed scanning speed of 2.0mm/s, the maximum compressive residual stress was induced at the laser power density of 31MW/mm2 ; and (4) for the fixed laser power density of 61 MW/mm2, that was induced at scanning speed of 1.0mm/s.

Journal

Citations (1)*help

See more

References(13)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top