- Evolution of Macroscopic and Microscopic Themal Cycle Damages in SP700/SCS-6 Titanium Alloy Matrix Composite
- 熱サイクルを受けるSP700/SCS-6チタン合金基複合材料のマクロ的およびミクロ的損傷発達
- ネツ サイクル オ ウケル SP700 SCS 6 チタン ゴウキンキ フクゴウ ザイリョウ ノ マクロテキ オヨビ ミクロテキ ソンショウ ハッタツ
この論文をさがす
抄録
Damage evolution process of a new generation titanium alloy matrix composite, SP-700/SCS-6, was studied when the composite was subjected to thermal cycles at elevated temperatures. Two types of damages were focused on : one is the macroscopic damage, or thermal cycle cracking induced by the repeat of thermal stress ; and the other is the microscopic damage, or microstructural change of the fiber/matrix interface characterization. The investigation on the former showed that the cracks were originated and propagated, associated with the following behavior : the crack propagation rates almost linearly increased with the crack length at the early growth stage, and then they gradually decreased and finally arrested in the most cases. This behavior was shown to be rationalized on the basis of fracture mechanics law. The analysis of the interface by means of a transmission electron microscope and an energy dispersive X-ray spectrometer (EDS) demonstrated that the products of the interface reaction zone, as well as the thickness, were changed by the repeat of thermal cycles. However, the thickness was still significantly thinner, compared with that in other kinds of titanium alloy matrix composite systems.
収録刊行物
-
- 材料
-
材料 54 (3), 271-278, 2005
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205418674432
-
- NII論文ID
- 110006266485
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 7284146
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可