- Crack Growth Behavior in Low <i>ΔK</i> Region in Corrosive Solutions for 13Cr Stainless Steel
- 13Crケイ コウ ノ フショク カンキョウカ ノ テイ デルタKリョウイキ
この論文をさがす
抄録
Corrosion fatigue crack growth tests in low ΔK region in 3%NaCl solution and in distilled water have been carried out on 13Cr stainless steels at various stress ratios (R=-1.0, 0.1, 0.4, 0.8). The effect of frequency on corrosion fatigue crack growth in 3%NaCl solution was also investigated. The results are summarized as follows.<br>(1) The corrosive environment studied here had little effect on crack growth rate in ΔK≥ΔKth (ΔKth: threshold value in air) for R=-1.0 and 0.1, but it slightly increased the crack growth rate for R≥0.4.<br>(2) As critical crack growth rate dropped from (2∼5)×10-10m/cycle in air to (2∼5)×10-11m/cycle in 3%NaCl, ΔKthCF(ΔKthCF: threshold value in corrosive environment) decreased 0.4 times (R=-1.0) to 0.6 times (R=0.1) of ΔKth. ΔKthCF in distilled water was (0.65∼0.70) time (R=-1.0 and R=0.1) of ΔKth.<br>(3) Corrosion pits often occurred at the corrosion fatigue crack tip in the region below da/dN=(2∼8.7)×10-11m/cycle. Therefore, the ΔK value required to reinitiate crack growth from those pits was about 1.5 times higher than that of ΔKthCF.<br>(4) The crack growth law derived previously by considering the effects of waveform and frequency was also found valid as the first approximation for the materials tested.
収録刊行物
-
- 材料
-
材料 33 (370), 914-920, 1984
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205418892416
-
- NII論文ID
- 110002301266
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 2997230
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可