書誌事項
- タイトル別名
-
- Evaluation of Mechanical Properties and Nano-Structure Analysis of Au-20Sn and Au-12Ge Solders
- Au-20SnおよびAu-12Geはんだの力学特性評価とナノレベル組織解析
- Au 20 Sn オヨビ Au 12 Ge ハンダ ノ リキガク トクセイ ヒョウカ ト ナノレベル ソシキ カイセキ
この論文をさがす
説明
Au alloys have great potentialities as solder joints of electronic packaging. However, studies on mechanical properties of Au solders, especially on creep properties, are very limited. Mechanical properties of Au-20Sn and Au-12Ge were measured by indentation tests ranging between nano and macro scales. First, macro indentation creep tests were carried out at various temperatures, i.e. 295K, 323K, 373K, 398K and 423K. It was found that the indentation creep deformation was observed at room temperature for Au-20Sn, while above 373K for Au-12Ge. Second, the indentation creep properties were measured for ζ and δ phases of Au-20Sn using a nano-indentation testing machine in order to investigate the influences of microstructure on the creep properties. Finally, we evaluated anisotropy of textured microstructure of Au-12Ge, where the dent shapes were distorted. This behavior was attributed to the three dimensional configurations, namely pile-up and sink-in. Based on the results of nano-indentation tests, numerical model for the microstructure of Au-12Ge was established and the mechanisms of the pile-up and sink-in were discussed.
収録刊行物
-
- 材料
-
材料 56 (10), 913-919, 2007
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205419124096
-
- NII論文ID
- 130002085983
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 8976728
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可