Structural Control of Porous Fly-Ash and Flexural Strength by Zeolitization

DOI Web Site 2 Citations 6 References

Bibliographic Information

Other Title
  • 多孔質フライアッシュの組織制御とゼオライト化による強度変化
  • タコウシツ フライアッシュ ノ ソシキ セイギョ ト ゼオライトカ ニ ヨル キョウド ヘンカ

Search this article

Description

The porous fly-ash ceramics with various porosity were prepared using colloidal process with molten wax. Polyethylene terephthalate powders were used combustible pore-forming agents. The total porosity of porous fly-ash increased with the polyethylene terephthalate powder content. The flexural strength of porous fly-ash drastically decreased as the total porosity increased. By the treatment of the sintered fly-ash with 3mol/dm3 NaOH solution at 383K for 15h, phillipsite, a kind of zeolite, was formed on the sintered fly-ash surface. The flexural strength of sintered fly-ash decreased to half of the original value by the zeolitization treatment.

Journal

Citations (2)*help

See more

References(6)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top