Examination of Behaviour of Fatigue Cracks in Carbon Steel Using Slip-initiation Phenomenon

DOI Web Site

Bibliographic Information

Other Title
  • 炭素鋼におけるすべり線発生現象を利用した疲労き裂の挙動の検討
  • タンソ コウ ニ オケル スベリセン ハッセイ ゲンショウ オ リヨウシタ ヒ

Search this article

Description

In order to examine the behaviour of fatigue cracks in carbon steel subjected to rotary bending and cyclic torsion, both the technique utilizing slip-initiation phenomenon in the material and the copper electroplating method of stress analysis are applied. Based on the above results, the fatigue-notch factor of cracked specimens is compared with the stress-concentration factor at crack tip. It is found that more accurate results can be obtained by the slip-initiation technique than by the electroplating method, if the measuring region at the crack tip is identical. The change in metal properties caused by the formation of fatigue cracks has no effect on the crack propagating stress in pure iron, but it affects notably the crack propagating stress in eutectoid steel.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top