Rotating bending fatigue tests were carried out for maraging steels nitrided under three conditions in order to investigate the influence of nitriding on fatigue strength. The fatigue strength was increased due to nitriding. The increase in fatigue strength and the fracture mechanism were markedly influenced by nitriding condition. That is, fracturing of the steel nitrided at under-aging condition, 480°C-1h and 5h, occurred from the surface of the specimen in the short life region, and from the interior in the long life region, although all of the specimen aged at under and over-aging conditions and nitrided at over-aging condition, 570°C-1h, fractured from the surface. Consequently, S-N curves in the former steel showed a two-step shape. The fatigue strength decreased with the increase in nitriding time in the short life region where the surface fracture occurred, though there is no or little influence of nitriding time on the fatigue strength in the long life region where the internal fracture occurred. The decrease in the fatigue strength was related to the surface brittleness caused by longer nitriding.

収録刊行物

  • 材料

    材料 52 (11), 1331-1336, 2003

    公益社団法人 日本材料学会

被引用文献 (2)*注記

もっと見る

参考文献 (23)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ