Fatigue Strength of Laser-Processed Hot Work Tool Steel and Its Reliability

DOI Web Site 1 Citations 9 References

Bibliographic Information

Other Title
  • レーザ処理された熱間工具鋼の疲労強度特性と信頼性評価
  • レーザ ショリ サレタ ネッカン コウグ コウ ノ ヒロウ キョウド トクセイ ト シンライセイ ヒョウカ

Search this article

Abstract

A fatigue life of die-casting dies depends on heat checks, which are fine shallow cracks on a surface due to cyclic thermal stress. According to the recent study, the laser-processing is effective to repair cracks and extend the life of dies. Therefore, the purpose of this study is to evaluate the fatigue strength of laser-processed hot work tool steel to validate the reliability of repaired dies.<br>In this study, the rotating bending fatigue test for the laser-processed hot work tool steel specimens has been carried out. Because test results have scatter, S-N curves are decided based on the evaluation of fatigue strength distribution. As a result, the fatigue strength of the laser-processed specimens decrease remarkably in compared with that of the non-processed ones. The notch sensitivity might have risen because the structure became brittle due to rapid cooling. However, it can be recovered by heat-treatment at 773K. This could be due to a high yield strength resulted in a secondary-hardening effect. The fractgraphic results also demonstrate the same tendency. The fracture surface of heat-treated specimen is similar to that of base metal, while that of laser-processed one shows different appearance.<br>The laser-processing method can be carried out at relatively low cost and effective for the repair of heat check. Therefore, we can conclude that this method is available for the extension of the life span of dies.

Journal

Citations (1)*help

See more

References(9)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top