- A Study of Mechanical Properties and Morphological Change of Polypropylene/Polyamide with Addition of PP-g-MAH through Reactive Processing Method
- RPホウ オ モチイタ PP/PA6/マレインサン ヘンセイ PP ブレンド ザイリョウ ノ リキガク ブッセイ カイシツ ギジュツ
この論文をさがす
抄録
In this study, mechanical properties and morphological change of polypropylene (PP) and polyamide 6 (PA6) blend prepared by reactive processing (RP) with addition of PP-grafted maleic anhydride (PP-g-MAH) as a compatibilizer was investigated. As RP methods, three different procedures for feeding PA6 and/or PP-g-MAH through side feeder were employed and two different types of PP-g-MAH were used. The PP/PA6 blends obtained by feeding PA6 and PP-g-MAH through side feeder (Tp.Sn.c) showed high mechanical properties: the elongation at break increased up to 700% and the domain size of PA6 phase decreased dramatically from 29μm to 1.6μm. Although the modulus and the elongation at break of PP/PA6 blend with PP-g-MAH increased with the amount of PP-g-MAH, they reached constant values up to 3 or 5 phr in both cases of KY-H and KY-L. Furthermore, it was found that the degree of crystallinity of PP decreased and PA6 in the PP/PA6 blend can be changed with the amount of PP-g MAH.
収録刊行物
-
- 材料
-
材料 62 (1), 1-7, 2013
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205443434624
-
- NII論文ID
- 130003367116
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BC3sXlvFaksr8%3D
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 024238763
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可