- Thickness Effect of Interlayer on Fatigue Behavior and Fatigue Fracture A5052 Mechanisms in Aluminum Alloy with DLC/Thermally Sprayed WC-12Co Hybrid Coatings
- DLC/WC-12Co ヨウシャ フクゴウ ヒマク オ ユウスル アルミニウム ゴウキン A5052 ノ ヒロウ キョドウ ニ オヨボス チュウカンソウ アツサ ノ エイキョウ オヨビ ヒロウ ハカイ キコウ
この論文をさがす
抄録
WC-12Co was thermally sprayed by a high velocity oxygen fuel (HVOF) method on A5052 aluminum alloy as an interlayer with the thicknesses of 25, 70 and 120μm and subsequently diamond-like carbon (DLC) film was deposited with the thickness of 15μm to fabricate DLC/WC-12Co hybrid coating. Rotary bending fatigue tests were conducted using the specimens with DLC/WC-12Co hybrid coating, DLC single coating, WC-12Co single coating and without coating, and the thickness effect of interlayer on the fatigue behavior was investigated. The fatigue strengths of the specimens with DLC single coating and WC-12Co single coating were higher than those of the substrate specimens. The fatigue strengths in the specimens with WC-12Co single coating increased with increasing the thickness of WC-12Co layer. The specimens with hybrid coating exhibited higher fatigue strengths than the specimens with WC-12Co single coating when the thickness of WC-12Co layer was the same. However the thicker WC-12Co interlayer led to the lower improvement of fatigue strength by hybrid coating. In the specimens with WC-12Co layer, the boundary between WC-12Co layer and substrate was rough and uneven due to the thermal spray process and a fatigue crack initiated at the concave site of substrate on the boundary. In the specimens with hybrid coating, cracking in DLC film and WC-12Co interlayer occurred simultaneously and suddenly near the end of fatigue life. A fatigue crack in the substrate had grown up to a large size and the specimen fractured soon after a crack appeared on the surface.
収録刊行物
-
- 材料
-
材料 62 (12), 738-743, 2013
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205443627136
-
- NII論文ID
- 130003384114
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 025098090
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可