The compressive strength and the electrical resistivity of mortar specimens using mineral admixture (fly ash and ground granulated blast-furnace slag) were measured to evaluate the influence of mineral admixture on the mortar hardening process. Comparing the changes in compressive strength and electrical resistivity of mortar using the mineral admixture was compared, compressive strength tended to start increasing from a relatively early stage, while electrical resistivity tended to increase after a slight delay. The formation factor variation shows that the increase in electrical resistivity is due to changes in the pore structure, such as tortuosity, rather than changes in the pore solution concentration. Then, the apparent diffusion coefficient of chloride ion was estimated from electrical resistivity. The diffusion coefficient of mortar using blast-furnace slag tended to fall below that of ordinary Portland cement at 7days, and then gradually improved. Until 14days, the diffusion coefficient of mortar using fly ash exceeds that of ordinary Portland cement mortar, but declines below the latter after 91days. This study shows that the periods of the surge in permeability and compressive strength differ, and that these features vary depending on the type of mineral admixture used.
収録刊行物
-
- 材料
-
材料 62 (8), 479-485, 2013
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205444260992
-
- NII論文ID
- 130003367205
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BC3sXhsFOru77P
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 024846081
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可