- Microstructural Changes and Type-IV Damage Evolutions during Creep in High Cr Steel Welds
- コウCr タイネツコウ ノ ヨウセツブ ニ オケル クリープ チュウ ノ ソシキ ヘンカ ト Type-Ⅳ ソンショウ キョドウ
この論文をさがす
抄録
Creep strength of high Cr ferritic steel welds decreases than base metals due to Type-IV creep damages formed in the heat affected zone (HAZ) during long-term use at high temperatures. In the present study, creep tests of ASME Gr.91 and Gr.122 steel welded joints were interrupted at several time steps at 600°C. Microstructural changes and damage behaviors in the fine-grained HAZ of welds during creep were investigated by using SEM, TEM, and EBSD. KAM, grain boundary length and hardness of fine-grained HAZ decreased till 0.2 of life and saturated in the Gr.91 steel weld, whereas they decreased after 0.5 of life in the Gr.122 steel weld. It was found that the recovery of dislocation structures in the fine-grained HAZ was completed at early stage of life for the Gr.91 steel weld, whereas it occurred in the later stage of life for the Gr.122 steel weld. These differences of microstructural changes was considered to relate to the differences of Type-IV creep damage behavior; early initiation of creep voids at 0.2 of life in the Gr.91 steel weld and later damage evolution after 0.5 of life in the Gr.122 steel weld.
収録刊行物
-
- 材料
-
材料 62 (2), 75-81, 2013
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205445876864
-
- NII論文ID
- 130003367139
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 024295721
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可