ウレタン系ラテックスバインダーを用いたZrO<sub><font size="-1">2</font></sub>スラリーの一方向凍結成形による多孔体の作製

書誌事項

タイトル別名
  • Preparation of Porous ZrO<sub><font size="-1">2</font></sub> Ceramic by Unidirectional Freeze Casting of the Slurry Containing Urethane Latex Binder
  • ウレタン系ラテックスバインダーを用いたZrO₂スラリーの一方向凍結成形による多孔体の作製
  • ウレタンケイ ラテックスバインダー オ モチイタ ZrO ₂ スラリー ノ イチホウコウ トウケツ セイケイ ニ ヨル タコウタイ ノ サクセイ
  • Preparation of Porous ZrO2 Ceramic by Unidirectional Freeze Casting of the Slurry Containing Urethane Latex Binder

この論文をさがす

抄録

ZrO2 porous ceramic was prepared by a unidirectional freeze casting using aqueous slurries containing urethane latex binder. The effects of solid loading, binder content and cooling rate on the pore size distributions of sintered bodies were investigate by scanning electron microscopy and mercury intrusion porosimetry. Porous ZrO2 ceramic with continuously long-ranged pore structure was obtained by the unidirectional freezing of the aqueous ZrO2 slurry, followed by sublimation of ice and firing at 1400°C for 1h in air. The solid loading of the slurry scarcely affected the pore size of sintered bodies. However, the pore volume decreased and the thickness of pore wall increased with increasing solid content in the slurry. Binder content largely influenced the strength of green bodies. At low binder content, green bodies became weaker, and therefore many cracks were generated bodies. The effect of cooling rate on the sintered body was small, but pore size decreased with increasing cooling rate. These results show that the pore size and volume can be controlled by modifying the cooling rate of the slurries and slurry concentration.

収録刊行物

  • 材料

    材料 62 (6), 362-366, 2013

    公益社団法人 日本材料学会