多結晶Ni基超合金の室温疲労き裂進展に及ぼす結晶粒の方位と粒界の影響

DOI Web Site 被引用文献1件 参考文献5件 オープンアクセス

書誌事項

タイトル別名
  • Influences of crystal orientations and grain boundary on crack propagation behaviour at room temperature in a polycrystalline Ni-base superalloy

説明

<p>Fatigue crack propagation in a polycrystalline Ni-base superalloy was experimentally investigated at room temperature. Fatigue crack propagation tests were conducted under a constant ΔK condition to clarify the effect of grains crystal orientation, grain size and grain boundary, employing CT specimens with different grain size and grains orientations. A series of experiments revealed that crack propagation modes within the grain were roughly categorized into the shearing and opening mode, depending on crystal orientations and grain size. Crack propagation rate in the shearing mode was affected by the primary and secondary crystal orientation of grains and its fundamental mechanism could be explained by the findings for the single crystal material in our previous study. The crack propagation rate in the opening mode was affected by both Schmid factor and Young's modulus, which increased with reduction of the crack length relative to the grain size. It was also found that the grain boundary caused the crack retardation depending on the crack propagation modes in both grains across the boundary. In case the crack propagated in the shearing mode in two adjacent grains, the crack retardation became more pronounced due to the discontinuity and transition of the crack planes.</p>

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (5)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ