書誌事項
- タイトル別名
-
- Verification and improvement of power generation under the uniform temperature environment by the poly-crystalline clathrate
- 多結晶クラスレートによる等温環境下での発電の検証および向上
- タケッショウ クラスレート ニ ヨル トウオン カンキョウ カ デ ノ ハツデン ノ ケンショウ オヨビ コウジョウ
この論文をさがす
説明
<p> A novel electric power generation different from the Seebeck effect by using poly-crystaline Ba8AuxSi46-x clathrate consisted of two layers, n-type and p-type materials, was devised. In order to investigate composition dependence of generated voltage, poly-crystalline clathrate samples consisted of two layers with various Au composition were prepared by SPS method. According to composition analysis, the mixed layer was formed at the interface of two layers. The sample consisted of n-type Ba8Au4.5Si41.5 / p-type Ba8Au5.5Si40.5 can generate around 2.0 mV at 723 K under no temperature difference. It is considered that this voltage was caused by charge separation with the diffuse of electrons and holes exited at mixed layer with narrower band gap part on interface. Ba8Au4.0Si42.0 / Ba8Au6.0Si40.0 and Ba8Au4.8Si41.2 / Ba8Au5.2Si40.8 samples showed around 4.0 and 1.0 mV at 723 K, respectively. These results suggested that the voltage increased with difference of Fermi level between n- and p-type semiconductors. </p>
収録刊行物
-
- 傾斜機能材料論文集
-
傾斜機能材料論文集 31 (0), 29-32, 2017
傾斜機能材料研究会