<p>Cotton fabrics were oxidized with sodium dichloroisocyanurate (SDIC) and catalytic amounts of 2,2,6,6-tetramethylpiperidin-1-oxyl (TEMPO) and NaBr in water at pH 9 or 10 and temperatures of 15–40 ̊C for 5–15 min. The TEMPO-oxidized fabrics were post-treated with NaClO2,H2O2 and NaBH4. The oxidized cotton fabrics thus obtained had higher carboxylate contents and higher viscosity-average degrees of polymerization(DPv), compared with the conventional TEMPO/NaBr/NaClO or TEMPO/NaClO/NaClO2 system when the oxidation was carried out under similar conditions. Because SDIC gradually releases HOCl in water, forming NaOCl at pH 10, this NaClO is preferentially consumed for oxidation of C6-primary hydroxyl groups of cellulose, rather than cellulose depolymerization or formation of C2/C3 ketones. As a result, the decrease in whiteness of the oxidized cotton fabrics without post NaBH4 treatment after heating was lower than those prepared with TEMPO/NaBr/NaClO system. Moreover, the TEMPO/NaBr/SDIC oxidation of cotton fabrics can be carried out in water at pH 9, which leads to the same carboxylate content as that prepared in water at pH 10 but higher DPv. Thus, the TEMPO/NaBr/SDIC is an efficient and promising system for oxidation of cotton fabrics with high carboxylate contents and high DPv values, suitable for functionalization of cotton fabrics for clothes and underwear.</p>
収録刊行物
-
- Journal of Fiber Science and Technology
-
Journal of Fiber Science and Technology 72 (8), 172-178, 2016
一般社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205763537024
-
- NII論文ID
- 130005261054
-
- ISSN
- 21897654
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可