P-1-1 Preparation of high-surface-area activated carbon from peat
-
- Javzandolgor Bud
- Hokkaido University
-
- Nishio Megumi
- Hokkaido University
-
- Mochizuki Yuuki
- Hokkaido University
-
- Tsubouchi Naoto
- Hokkaido University
Bibliographic Information
- Other Title
-
- P-1-1 泥炭からの高表面積活性炭の製造
Abstract
<p>The optimum preparation conditions of high-surface-area activated carbon (AC) from peat, urea and natural soda ash have been investigated with a flow-type quartz-made fixed bed reactor. Heating rate and pyrolysis temperature are 10 °C/min and 500-900 °C, respectively. The BET surface area of AC prepared from the mixture of peat/urea/Na2CO3 with mass ratio of 1.0/1.0/2.0 increases with increasing temperature and reaches about 1000 m2/g at 800 °C. When peat/urea/Na2CO3 mixing ratio is changed to 0.5-2.0/0.5-3.0/1.0-4.0, the surface area of AC prepared increases with increasing amount of urea. The N content of AC precursor strongly affects the surface area of AC. In addition, the XRD analyses of AC prepared show that the peak intensity attributable to C(002) increases with increasing temperature. It is thus likely that the optimum heat treatment temperature and mixing ratio are 800 °C and peat/urea/Na2CO3 = 1.0/1.0-3.0/2.0, respectively.</p>
Journal
-
- Proceedings of the Annual Conference of The Japan Institute of Energy
-
Proceedings of the Annual Conference of The Japan Institute of Energy 26 (0), 254-255, 2017
The Japan Institute of Energy
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205815486208
-
- NII Article ID
- 130005863615
-
- ISSN
- 24238325
- 24238317
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- CiNii Articles
-
- Abstract License Flag
- Disallowed