- OS2106 A Study of Cyclic High Stress Counts Dependence on fatigue Behavior for Bearing Steel in Rotating Bending under Decremental Step Loading
説明
In order to examine the fine granular area (FGA) formed timing in high cycle fatigue for bearing steel, the rotating bending tests were carried out under two conditions of decremental step loading. The cumulative damage value of stress cycles at the high stress level was 0.1 against the average of the fatigue life in the interior inclusion induced fracture. And the cumulative damage values were 0.14 and 0.32 against the average of the fatigue life in the surface induced fracture. In this experiment, the roll processing performed in order to improve a fatigue life in surface induced fracture mode. From the experimental results, the different fine granular area aspect from stress constant cases was observed.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2012 (0), _OS2106-1_-_OS2106-3_, 2012
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205870705024
-
- NII論文ID
- 110009937539
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可