- Evaluation of stress degradation under high temperature creep of Ni-base super alloy
抄録
<p>In order to investigate the damage mechanism in a grain of the directionally solidified Ni-base super alloy (CM247LC) under creep loading, the tensile strength of the alloy with creep damage wasmeasured by using the micro-tensile test method . The as-received sample mainly showed ductile fracture mode with little necking around the fracture surface and the estimated strength was about 1050 MPa. This value agreed well with the strength of the macro specimen. Then, the degradation of the tensile strength of this alloy was evaluated by measuring the change in the strength of the grain with creep damage.</p>