OS0706 Effect of loading mode on very high cycle fatigue properties in high-speed tool steel

DOI Web Site

Bibliographic Information

Other Title
  • OS0706 高速度工具鋼の超高サイクル疲労強度特性に及ぼす荷重負荷様式の影響(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)

Abstract

In order to study the effect of loading mode on fatigue properties of high-speed tool steel (0.7C-3 Mo-2V) in very high cycle regime, fatigue tests under axial loading and rotating bending condition were performed in laboratoiy air using the hourglass shaped specimen. From the experiment results, clear duplex S-N curve appeared in both loading conditions, that is, there were two curves composed of a surface failure mode and a subsurface failure mode. Fatigue life under axial loading condition was shorter than that under the rotating bending condition, especially in low stress amplitude level. The difference in fatigue lifetime and transition of failure mode between the loading modes was discussed from the viexoint of inclusion size, applied stress distribution across the specimen section and residual stress in surface layer.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top