OS0707 Rotary bending fatigue strength of developed high-speed tool steels in very high cycle regime

Bibliographic Information

Other Title
  • OS0707 開発マトリックスハイスの超高サイクル回転曲げ疲労強度特性評価(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)

Abstract

In order to evaluate the fatigue strength in very high cycle regime of newly developed two kind of high-speed tool steels, such as, MHS5 (0.9C-2W-2V-3Mo) and MH2 (0.5C-0.5V-2Mo-0.1Nb), rotary bending fatigue test was carried out inlaboratoiy air at room temperature using a hourglass shaped specimen S-N curve obtained from MHS5-specimen appeared to have a stepwise shape with a horizontal asymptote changing from the surface carbide induced failure mode (S-mode) in high stress amplitude level to the subsurface carbide induced one with GBF area in low stress amplitude level. On the other hand, transition of failure mode in MHS2-specimen was occurred from the S-mode in high stress amplitude level to crystal-slip induced failure mode formed in the specimen surface. It was suggested that the difference of failure mode in very high cycle regime between tested materials was caused by the size of carbide particles precipitated in the matrix.

Journal

Details 詳細情報について

Report a problem

Back to top