- 226 Characteristic improvements of sintered compacts by controlling particle size distribution of atomized ferrous alloy powders
抄録
Effect of particle size distribution on the density and shrinkage of atomized ferrous alloy powder compacts were investigated by controlling particle size distribution of the two bimodal ferrous alloy powders (-25μm / 125-150μm, 25-46μm / 125-150μm). These powders were sintered at 1473K in vacuum after compacted at the pressure of 490MPa. As a result, the sintered compact of -5μm / 125-150μm bimodal powder with fine powder content of 35 mass% showed higher density and lower shrinkage ratio than those of other powder compacts. The improvement of particle packing depends strongly on the size ratio, mixing compositions of the fine to coarse powder. The density increase by the fine powder addition is considered to improve the mechanical properties of the sintered compacts without further addition of alloying elements.
収録刊行物
-
- 機械材料・材料加工技術講演会講演論文集
-
機械材料・材料加工技術講演会講演論文集 2010.18 (0), _226-1_-_226-3_, 2010
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205877348864
-
- NII論文ID
- 110008743002
-
- ISSN
- 2424287X
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可