  • On the Crack Length and the Low Temperature Brittleness of a Carbon Steel Subjected to Corrosion Fatigue
  • フショク ツカレ オ ウケタ コウザイ ノ キレツ フカサ ト テイオンゼイ セイ ニ ツイテ

この論文をさがす

抄録

The lengths of the cracks formed by the corrosion fatigue in saline are studied on the smooth specimens of a carbon steel, and the effect of corrosion fatigue on the low temperature brittleness is discussed. The cracks occur at early stage of the fatigue life and the cyclic rates of their propagation dl/dN depend on the actual stress σck repeated at the root of the crack, where k represents the notch effect of corrosion pits increasing with time. The transition temperature Tr °C. of the specimens having the cracks caused by corrosion fatigue and the rate of its change with cycle ΔTr/ΔN rise with increasing of cyclic ratio. It also rises according to the increase of square root of crack length l1/2, having no relation to the nominal stress σc of the corrosion fatigue.

収録刊行物

詳細情報 詳細情報について

問題の指摘

ページトップへ