- Some Fundamental Properties of Galena
- ホウエンコウ ニ カンスル 1 , 2 ノ キソテキ セイシツ ニ ツイテ
- 示差熱分析および半導体的特性
- Differential thermal analysis and semiconductivity
この論文をさがす
抄録
The authors have investigated on the physical and chemical properties of galena produced from typical lead-zinc mines in Japan. Differential thermal analyses, thermal balance measurements, x-ray study and measurement of electrical properties were carried out. It was found that these properties are influenced by minor impurities. The main results obtained are as follows:<BR>(1) Differential thermal analysis curves showed two exothermic reaction at 770°C and 840°C, and a slight endothermic reaction at 850°-855°C.<BR>(2) According to the thermal balance measurement, weight began to increase at 310°C and changed to decrease at 750°C, a little inflection was observed on the decreasing curves at 850°-900°C.<BR>(3) Besides lead sulfide, lead sulfate, lead oxide and metallic lead were determined in the heated samples by x-ray spectrometer.<BR>(4) Because of minor impurities, exothermic reaction caused by oxidation of disordered samples began at lower temperature than that of ideal sample.<BR>(5) Semiconductivity of galena depends on its minor impurities, especially silver and bismuth.
収録刊行物
-
- 日本鑛業會誌
-
日本鑛業會誌 75 (856), 917-922, 1959
一般社団法人 資源・素材学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205981153024
-
- NII論文ID
- 130007254604
- 40018292766
-
- NII書誌ID
- AN00188932
-
- ISSN
- 21856729
- 03694194
-
- NDL書誌ID
- 9158103
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可