- SAITO Kozo
- 三井金属鉱業株式会社中央研究所
Bibliographic Information
- Other Title
-
- 方鉛鉱の濡れの性質について
- ホウエンコウ ノ ヌレ ノ セイシツ ニ ツイテ
Search this article
Abstract
The author have investigated on wetting characteristics of galena produced from Japan by means of spheroidal drop method. Advancing contact angles were affected with roughness and chemical composition of samples. A formation of new crystal on the surface of depressed galena was determined by electron diffraction method, and the wetting characteristics depend on nature of the crystal. The main results obtained are as follows:-<BR>(1) Contact angle depends on roughness of surface, and its value of fresh cleavage is greater than that of emery polished surface.<BR>(2) Contact angle is affected with chemical composition and its value decreases especially with increasing of silver content.<BR>(3) Contact angle of the sample preconditioned in potassium permanganate solution decreases linearly with increasing of concentration of the solution.<BR>(4) Surface of galena was slightly oxidized by potassium permanganate solution, and then manganese oxide hydrate MnO2·(0-1) MnO·nH2O was found on it by means of electron diffraction.
Journal
-
- Journal of the Mining and Metallurgical Institute of Japan
-
Journal of the Mining and Metallurgical Institute of Japan 77 (877), 471-476, 1961
The Mining and Materials Processing Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205981271424
-
- NII Article ID
- 40018292918
- 130007254823
-
- NII Book ID
- AN00188932
-
- ISSN
- 21856729
- 03694194
-
- NDL BIB ID
- 9158255
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed